Materials for Reinforced Concrete

Concrete is a composite material consists essentially of a) A binding medium cement and water called cement paste b) Particles of a relatively inert filler called aggregate

Materials for Reinforced Concrete

 

Concrete

 

Concrete is a composite material consists essentially of

 

a)     A binding medium cement and water called cement paste

 

b)    Particles of a relatively inert filler called aggregate

 

The selection of the relative proportions of cement, water and aggregate is called �mix design� Basic requirement of a good concrete are workability, strength, durability and economy. Depending upon the intended use the cement may be OPC (33,43 & 53 Grade), Rapid hardening cements Portland slag, Portland pozzolona etc. High cement content give rise to increased shrinkage, creep and cracking. Minimum cement content is 300Kg/m3 and maximum being 450Kg/m3 as per Indian code. Mineral additives like fly ash , silica fume, rice husk ash, metakoline and ground granulated blast furnace slag may be used to reduce micro cracks . The aggregate used is primarily for the purpose of providing bulk to the concrete and constitutes 60 to 80 percent of finished product. Fine aggregates are used to increase the workability and uniformly of concrete mixture. Water used for mixing and curing shall be clean and free from oil, acids, alkalis, salts, sugar etc. The diverse requirements of mixability, stability, transportability place ability, mobility, compatibility of fresh concrete are collectively referred to as workability.

 

Compressive strength of concrete on 28th day after casting is considered as one of the measure of quality. At least 4 specimens of cubes should be tested for acceptance criteria.

 

Grade of concrete

 

Based on the compressive strength of concrete, they are designated with letter H followed by an integer number represented characteristic strength of concrete, measured using 150mm size cube. Characteristic strength is defined us the strength of material below which not more than 5% of test results are expected to full. The concrete grade M10, M15 and M20 are termed as ordinary concrete and those of M25 to M55 are termed as standard concrete and the concrete of grade 60 and above are termed as high strength concrete. The selection of minimum grade of concrete is dictated by durability considerations which are based on kind of environment to which the structure is exposed, though the minimum grade of concrete for reinforced concrete is specified as M20 under mild exposure conditions, it is advisable to adopt a higher grade. For moderate, severe, very severe and extreme exposure conditions, M25, M30, M35 & M40 grades respectively are recommended. Typical stress-strain curves of concrete is shown in Fig.1.4



Reinforcing steel

 

Steel bars are often used in concrete to take case of tensile stresses. Often they are called as rebars, steel bar induces ductility to composite material i.e reinforced concrete steel is stronger than concrete in compression also. Plain mild steel bars or deformed bars are generally used. Due to poor bond strength plain bars are not used. High strength deformed bars generally cold twisted (CTD) are used in reinforced concrete. During beginning of 21st century, Thermo-mechanical tream (TMT) bars which has ribs on surface are used in reinforced concrete. Yield strength of steel bars are denoted as characteristic strength. Yield strength of mild steel is 250MPa, yield strength of CTD &TMT bars available in market has 415 MPa or 500 MPa or 550MPa. TMT bars have better elongation than CTD bars. Stress-strain curve of CTD bars or TMT bars do not have definite yield point, hence 0.2% proof stress is used as yield strength. Fig 1.5 shows stress strain curve of different steel grades. Steel grades are indicated by Fe followed by yield strength. In the drawings of RCC, denotes MS bar and # denotes CTD or TMT bars.




 

Tags : Civil - Design of Reinforced Concrete Elements - Methods Of Design Of Concrete Structures
Last 30 days 57 views
Related words :

What is Materials for Reinforced Concrete Define Materials for Reinforced Concrete Definition of Materials for Reinforced Concrete where how meaning of Materials for Reinforced Concrete lecturing notes for Materials for Reinforced Concrete lecture notes question and answer for Materials for Reinforced Concrete answer Materials for Reinforced Concrete study material Materials for Reinforced Concrete assignment Materials for Reinforced Concrete reference description of Materials for Reinforced Concrete explanation of Materials for Reinforced Concrete brief detail of Materials for Reinforced Concrete easy explanation solution Materials for Reinforced Concrete wiki Materials for Reinforced Concrete wikipedia how why is who were when is when did where did Materials for Reinforced Concrete list of Materials for Reinforced Concrete school assignment college assignment Materials for Reinforced Concrete college notes school notes kids with diagram or figure or image difference between Materials for Reinforced Concrete www.readorrefer.in - Read Or Refer

​TOP MENU

OTHER SUGEST TOPIC